Destination and fields of applications
Anticorrosion protection of steel articles and constructions, used in all atmospheric environments according to ISO 12944-5:2007.
Is used in complex coating systems as a covering layer in the absence of intensive effect of solar radiation.
Is recommended for using in coating systems with the enamel ISOLEP-mio, as well as other epoxy, polyurethane or organosilicon primers.
Certification, testing
The sanitary-and-epidemiologic finding ¹ 66.01.10.231.Ï.001728.05.06 dated 18.05.2006.
The finding is given by Research Institute for Lacquer Coatings with Experimental Machine-Building Plant «Viktoria».
Approbated by the Russian River Register.
General technical characteristics
| Coating |
| Colour and gloss of the coating |
Light grey (tint isn’t standardized); manufacturing of enamels of other colours is possible. |
| Thickness of 1-layer dry coating |
80 - 100 µm |
| Impact resistance |
500 mm, not less |
| Bend test |
20 mm, not more |
| Adhesion |
1 number, not more |
| Heat resistance |
150 °Ñ |
| Coating class |
V |
| Enamel |
| Density |
1,30 – 1,50 g/cm3 |
| Viscosity |
thixotropic |
| Non-volatile-matter content |
65 – 71 % |
| Theoretical rate for 1-layer coating |
220 – 270 g/m2 |
| Drying time to “touch-dry” state at temperature (20±2) °Ñ |
6 hours, not more |
| Viability after mixing at temperature (20±2) °Ñ |
12 hours, not less |
Reccomended condition of the painted surface
If necessary oils, lubricants and other adipose matters as well as moisture and dust are to be removed from the sized surface.
Application method
- The enamel base is to be thoroughly shuffled up to homogeneous state;
- While constant shuffling, curing agent is to be entirely injected into the base;
- Derived mixture is to be thoroughly shuffled and sustained before laying for not less than 30 minutes;
- It is recommended to dilute the enamel by solvent to operating viscosity directly before laying.
- The enamel is to be applied in plant and field environment at temperature from + 10 °Ñ to +40 °Ñ and relative air humidity from 85 %.
Cure time of the undercoat before applying the enamel ISOLEP at temperature (20+2) °Ñ is for:
- ñoating ZINEP – not less than 12 hours;
- ñoating ISOLEP-mio – not less than 12 hours.
Cure time of the coating before applying finishing layers is 7 days, before packing and shipment is not less than 24 hours.
Airless spraying
Recommended solvent - SOLV-UR or aromatics (xylene, Solvesso 100)
Quantity of solvent - from 5% to 8% by mass
Nozzle diameter - 0,33 – 0,53 mm
Pressure - 10 - 15 MPa (100 – 150 bar)
Air spraying
Recommended solvent - SOLV-UR or aromatics (xylene, Solvesso 100)
Quantity of solvent - from 5% to 8% by mass
Nozzle diameter - 1,8 – 2,2 mm
Pressure - 0,3 – 0,4 MPa (3 – 4 bar)
Brush / roller
Recommended solvent - SOLV-UR or aromatics (xylene, Solvesso 100)
Quantity of solvent - from 5% to 8% by mass
Cleaning of the equipment
SOLV-UR, aromatics (xylene, Solvesso 100) are used for rinsing painting equipment.
Packaging and storage
ISOLEP enamel is packed: base – in 10 liter metal pails and 1 liter metal cans, curing agent – in 3 liter metal pails or 0, 5 liter metal cans. Weight of the set packed into pails is 13 kilograms; one the set packed into cans is 1, 2 kilogram.
Storage conditions: the product is to be stored in an enclosed warehouse at environment temperature from -40˚C till +40˚C. While storage the container with the enamel isn’t to be subjected to precipitation and direct sun rays effect.
Warranty period of the enamel, determined by storage period of the enamel base in the manufacturer’s hermetically covered container is 12 months from the enamel due date.
Protective measures
See MSDS for the enamel ISOLEP.
|